PX314ZG

The PX314ZG is designed as a general purpose, cold curing flame retardant encapsulation resin. The system is similar to the very popular PX314R but uses a different hardener not subject to moisture inhibition. This means that a high level of cure can be achieved under cold, damp conditions even where small shot sizes are used.

Some important specifications of PX314ZG have been concluded into several points as follow. The first one is about its colour which would be black. The next one is about its specific gravity which would be 1.73 ± 0.02. The next one is about its viscosity which would be 11500 mPa.s. The next one si about its mix ratio by weight which would be 8.6:1. The next one is about its mix ratio by volume which would be 5.3:1. The next one is about its usable life which would be min 60. The next one is about its cure schedule which would be 24h.

Also there are some physical characteristics about PX314ZG. The first one is about its shore hardness which would be D/1:88 - D/15:85. The next one is about its heat deflection temperature which would be 50°C. The next one is about its operating temperature which would be from -40 to +115°C continuous and would be from -40 to +130°C short term. The next one is about its thermal conductivity which would be 0.38W/mK. The next one is about its tensile strength which would be from 55 to 59MPa. The next one is about its elongation at break which would be low. The next one is about its compressive tield strength which would be from 79 to 86MPa. The next one is about its tear resistance which would be low. The next one is about its lap shear strength which would be medium. The next one is about its shrinkage which would be low. And so on. For more information please contact us.