0402E050200NRR

The 0402E050200NRR has some points of structure that can be summarized as:(1)Main Material: Zinc Oxide;(2)End termination: Ag/Ni/Sn;(3)Packaging: Reel;(4)Complies with Standard: IEC61000-4-2 level 4;(5)Complies with RoHS Standard: Yes;(6)Lead content: < 1000ppm;(7)Reflow solder profile temperature (Recommend): 250 .

The absolute maximum ratings of the 0402E050200NRR can be summarized as:(1)Operating Temperature Range: -40 to +85;(2)Storage Temperature Range: -40 to +125;(3)Transient Response Time: < 50 ns.

The environmental characteristics of the 0402E050200NRR can be summarized as:(1)High Temperature Storage: The specimen shall be subjected to 150 ± 2 for 1000 ± 12 hours in a thermostatic bath without load and then stored at room temperature and humidity for 1 to 2 hours.;(2)High Temperature Load: For 1000± 2 hours, the specimen shall be stored at room temperature and humidity for one or two hours, the change of varistor voltage shall be within 10;(3)Low Temperature Storage: The specimen should be subjected to -40 ± 2, without load for 500 hours and then stored at room temperature for one or two hours..

The electrical characteristics of the 0402E050200NRR can be summarized as:(1)Maximum Allowable Voltage: Maximum continuous sine wave(RMS) or DC voltage which may be applied.;(2)Varistor Voltage: Voltage across the varistor measured at CmA DC.;(3)Max. Clamping Voltage: Peak voltage across the varistor with a specified peak impulse current of 8x20s waveform.;(4)Energy: The max. energy absorbed with a varistor voltage change of less than ±10% when one impulse (10x1000s) is applied.;(5)Leakage current: at V1mA*80% or at V1mA*80% (After Reliability Test);(6)Capacitance: Capacitance shall be measured at 1 kHz±10%,1 Vrms max.(1 MHz below 100 pF) 0V bias and 20±2. If you want to know more information about the 0402E050200NRR, please download the datasheet in www.seekic.com or www.chinaicmart.com .